Fit of metal-ceramic crowns: effect of coping fabrication method and veneering ceramic application

Aim: To evaluate the influence of cobalt-chromium (Co-Cr) coping fabrication methods and ceramic application on the marginal and internal fit of metal-ceramic crowns. Methods: Co-Cr copings for metal-ceramic crowns were prepared by lost wax casting or CAD-CAM machining of sintered blocks. The fit was analyzed using the silicone replica technique at four assessment points: marginal gap (MG), axial wall (AW), axio-occlusal (AO) angle, and central occlusal (CO) wall. After the initial analysis, the copings were ceramic-veneered with the layering technique, and the fit was again determined. Data were statistically analyzed by paired and unpaired Student's-t test (α=0.05). Results: Marginal and internal fit before ceramic application according to the coping manufacturing method showed significant differences only at CO (p < 0.001), with milled copings (137.98±16.71 µm) showing higher gap values than cast copings (112.86±8.57 µm). For cast copings, there were significant differences at MG (before 109.13±8.79 µm; after 102.78±7.18 µm) and CO (before 112.86±8.57 µm; after 104.07±10.63 µm) when comparing the fit before and after ceramic firing. For milled copings, there was significant difference only at AO (before 116.39±9.64 µm; after 108.54±9.26 µm). Conclusion: This study demonstrated that the coping fabrication method influenced the internal fit. Ceramic firing maintained or improved the fit of the metal-ceramic crowns. The marginal discrepancy of all restorations, before and after ceramic firing, can be considered clinically acceptable

Influence of sonic vibration and cement type on the bond strength of fiberglass posts after aging / Influencia de la vibración sónica y el tipo de cemento en la fuerza de unión de los postes de fibra de vidrio después del envejecimiento

Introduction: This study evaluated the influence of sonic vibration and thermocycling on the bond strength of fiberglass posts using conventional dual-cured and self-adhesive resin cements. Material and Methods: Ninety-six single-rooted endodontically treated teeth were divided randomly into eight groups according to the cement used (dual-cured or self-adhesive resin cement), use of sonic vibration during post accommodation, and aging conditions (24h in distilled water or 5,000 thermal cycles). The fiberglass posts (White Post DC1, FGM) were cleaned with alcohol, treated with silane and cemented with dual-cured (Allcem Core, FGM) or with self-adhesive resin cement (seT, SDI). For groups in which sonic vibration was used, the posts were accommodated, and sonic vibration was applied for 10 s using a special tip placed on top of the post (Sonic Smart Device, FGM). Pull-out tests were performed after storage in distilled water for 24h at 37°C or after thermocycling (5000 cycles, at 5°C and 55°C). The results were evaluated using three-way ANOVA and Tukey's test (α=0.05). Results: Significant differences were not observed between the bond strengths of dual-cured (87.93±41.81 N) and self-adhesive cement (82.53±41.43 N). Bond strength for the sonic vibration groups (100.36±42.35 N) was significantly higher than for groups without sonic vibration (70.13±34.90 N). There were significant differences between specimens subjected to thermocycling (98.33±39.42 N) and those stored for 24h in distilled water (72.16±39.67 N). Conclusion: It can be concluded that both sonic vibration and thermocycling significantly improved bond strength of fiberglass posts with the two evaluated resin cements.

Introducción: Este estudio evaluó la influencia de la vibración sónica y el termociclado en la fuerza de unión de los postes de fibra de vidrio utilizando cementos de resina autoadhesivos y de curado dual convencionales Material y Métodos: Se dividieron aleatoriamente noventa y seis dientes tratados endodónticamente de raíz única en ocho grupos según el cemento utilizado (cemento de resina de curado dual o autoadhesivo), el uso de vibración sónica durante la acomodación posterior y las condiciones de envejecimiento (24 horas agua destilada o 5.000 ciclos térmicos). Los postes de fibra de vidrio (White Post DC1, FGM) se limpiaron con alcohol, se trataron con silano y se cementaron con cemento de curado dual (Allcem Core, FGM) o con cemento de resina autoadhesivo (seT, SDI). Para los grupos en los que se utilizó vibración sónica, se acomodaron los postes y se aplicó la vibración sónica durante 10 s utilizando una punta especial colocada en la parte superior del poste (Sonic Smart Device, FGM). Las pruebas de extracción se realizaron después del almacenamiento en agua destilada durante 24 horas a 37ºC o después del termociclado (5000 ciclos, a 5ºC y 55ºC). Los resultados se evaluaron mediante ANOVA de tres vías y la prueba de Tukey (α = 0.05). Resultados: No se observaron diferencias significativas entre las resistencias de adhesión del cemento de curado dual (87,93 ± 41,81 N) y el cemento autoadhesivo (82,53 ± 41,43 N). La fuerza de unión para los grupos de vibración sónica (100,36 ± 42,35 N) fue significativamente mayor que para los grupos sin vibración sónica (70,13 ± 34,90 N). Hubo diferencias significativas entre los especímenes sometidos a termociclado (98,33 ± 39,42 N) y los almacenados durante 24 h en agua destilada (72,16 ± 39,67 N). Conclusión: Se puede concluir que tanto la vibración sónica como el termociclado mejoraron significativamente la fuerza de unión de los postes de fibra de vidrio con los dos cementos de resina evaluados.

Surface deterioration of indirect restorative materials

Abstract The objective of this work was to evaluate the effects of in vitro and in situ biodegradation on the surface characteristics of two resin cements and a hybrid ceramic system. One hundred and eighty specimens (4X1.5mm) of each material (Maxcem Elite, NX3 Nexus and Vita Enamic) were made and randomly distributed in twelve groups (n=15) according to the material and biodegradation method. The specimens were then submitted to the following challenges: storage in distilled water 37 ºC for 24 h or 7 days, storage for 7 days, at 37 ºC, in stimulated saliva or in situ. The in situ stage corresponded to the preparation of 15 intraoral palatal devices, used for 7 days. Each device presented 3 niches, where a sample of each materials was accommodated. Specimens from both saliva and in situ groups suffered a cariogenic challenge, corresponding to the application of a solution of 20% of sucrose, 10 times throughout each day. After each biodegradation method, the surface roughness (Ra), Vickers hardness (VHN) and scanning electron microscopy (SEM) analyzes were performed. The data collected were evaluated by Levene test, two-way ANOVA and Tukey`s test (α=5%). The in situ challenge promoted the greater biodegradation, regardless of the material. Regarding the materials, the Vita Enamic VHN was negatively affected by all biodegradation methods and the Nexus NX3 presented better performance than the self-adhesive cement tested. Therefore, within the conditions of this work, it was concluded that in situ biodegradation can affect negatively the surface characteristics of indirect restorative materials.

Resumo O objetivo deste trabalho foi avaliar os efeitos da biodegradação in vitro e in situ nas características superficiais de dois cimentos resinosos e de um sistema cerâmico híbrido. Cento e oitenta espécimes (4X1,5mm) de cada material (Maxcem Elite, NX3 Nexus e Vita Enamic) foram distribuídos aleatoriamente em doze grupos (n=15) de acordo com o material e o método de biodegradação. Os espécimes foram então submetidos aos seguintes desafios: armazenamento em água destilada 37ºC por 24 horas ou 7 dias, armazenamento por 7 dias, a 37ºC, em saliva estimulada ou in situ. O estágio in situ correspondeu à preparação de 15 dispositivos intra-orais palatinos, utilizados por 7 dias. Cada dispositivo apresentou 3 nichos, onde uma amostra de cada material foi acomodada. As amostras dos grupos saliva e in situ sofreram um desafio cariogênico, correspondendo à aplicação de uma solução de 20% de sacarose, 10 vezes ao longo de cada dia. Após cada método de biodegradação, foram realizadas as análises de rugosidade superficial (Ra), dureza Vickers (VHN) e microscopia eletrônica de varredura (MEV). Os dados coletados foram analisados por meio do teste de Levene, ANOVA two-way e teste de Tukey (α=5%). O desafio in situ promoveu maior degradação, independentemente do material. Em relação aos materiais, a VHN do Vita Enamic foi afetada negativamente por todos os métodos de degradação e o Nexus NX3 apresentou melhor desempenho que o cimento autoadesivo testado. Portanto, dentro das condições deste trabalho, concluiu-se que a biodegradação in situ pode afetar negativamente as características superficiais de materiais restauradores indiretos.

Long-term color stability of orthodontic adhesives after exposure to different staining agents

Context: The aims of this study were (i) to evaluate the color stability of two orthodontic adhesives and (ii) to evaluate the color stability of enamel and ceramic brackets bonded with orthodontic adhesives after exposure to different staining agents. Materials and Methods: Disks were prepared with two orthodontic adhesives (Transbond and Enlight). Color stability evaluation was performed with a spectrophotometer using CIELab parameters. The specimens were divided into four groups and immersed in the following staining agents (n = 5): distilled water (control), coffee, red wine, and cola soft drink, for 1 h/day for 120 days. Twenty molar crowns were also used. The baseline color of enamel was obtained and ceramic brackets were bonded with the orthodontic adhesives. The enamel specimens were divided into four groups and immersed in the same staining agents. After 120 days, another color reading with the brackets in position was taken. The brackets were then removed and the enamel color was again evaluated. Color difference (ΔE) in different time periods was determined and the data were analyzed by ANOVA and Tukey's test (α = 5%). Results: Transbond showed lower ΔE than Enlight. Water, cola, and coffee had the lowest ΔE values. Immersion in wine showed the highest ΔE values. For time, the lower ΔE values were found for 24 h and 7 days. Storage times of 60, 90, and 120 days showed the highest ΔE values. ΔE for enamel showed significant differences only for time. Conclusion: Adhesive, staining agents, and storage time influenced the color stability of orthodontic adhesives.

Influence of pre-curing different adhesives on the color stability of cemented thin ceramic veneers

Abstract The objective was to evaluate the color stability of thin ceramic veneers as a function of the curing mode (with and without pre-cure) of different adhesive systems applied to the internal surface of ceramics. Five adhesive systems (Scotchbond Multi-Purpose, Single Bond Universal, Gluma 2 Bond, Ambar, and Ambar APS) and photo-cured resin cement (Allcem Veneer) were used for cementing 0.6 mm-thick feldspathic veneers (Mark II) on composite resin substrates (Charisma Diamond). The groups, according to adhesive system, were divided into two subgroups (n=10): i) adhesive and resin cement were polymerized separately (pre-cure of the adhesive), ii) adhesive and resin cement were polymerized simultaneously. The CIELab color parameters were determined with a spectrophotometer at 24h (baseline), 7 days, 30 days and 12 months. Data were analyzed by two-way ANOVA and Tukey's test (α=0.05). The results indicated statistically significant differences for adhesive systems and time. The mode of curing of the adhesive system was not statistically significant: pre-cured adhesives (2.6±1.3) and not pre-cured adhesives (2.8±1.4). For the adhesives, ΔE values varied in the following order: Ambar-APS (1.6±0.5) < Scotchbond Multi-Purpose (2.6±1.2) = Gluma 2 Bond (2.7±1.2) = Ambar (2.9±1.2) < Single Bond Universal (3.5±1.5). For time, ΔE values were: 7 days (1.7±0.7), 30 days (3.5±1.2) and 12 months (2.9±1.3). It can be concluded that the different adhesive systems used for cementing thin ceramic veneers influenced the final color of the indirect restorations. The adhesives curing mode did not present a significant effect in the color stability of thin ceramic veneers.

Resumo O objetivo deste estudo foi avaliar a estabilidade de cor de laminados cerâmicos de espessura fina em função do momento de ativação de diferentes sistemas adesivos na superfície interna das cerâmicas. Foram utilizados 5 sistemas adesivos (Scotchbond Multiuso, Single Bond Universal, Gluma 2 Bond, Ambar and Ambar APS) e o cimento resinoso fotoativado (Allcem Veneer) para cimentação de lâminas de cerâmica feldspática (Mark II) com 0,6 mm de espessura, sobre substratos de resina composta (Charisma Diamond). Os grupos, de acordo com o sistema adesivo utilizado, foram divididos em dois subgrupos (n=10): i) adesivo e cimento resinoso foram polimerizados separadamente (polimerização isolada do adesivo), ii) adesivo e cimento resinoso foram polimerizados ao mesmo tempo (polimerização simultânea). Os parâmetros de cor do sistema CIELab foram determinados com um espectrofotômetro nos tempos de 24 h (baseline), 7 dias, 30 dias e 12 meses. Os dados foram analisados por ANOVA a dois fatores e teste de Tukey (α=0,05). Os resultados indicaram diferenças estatísticas significantes para os sistemas adesivos e tempo. O momento da fotoativação do sistema adesivo não foi estatisticamente significante: polimerização prévia (2,6±1,3) e polimerização simultânea (2,8±1,4). Para o sistema adesivo, os valores médios de ΔE variaram na seguinte ordem: Ambar APS (1,6±0,5)<Scotchbond Multi-Purpose (2,6±1,2)=Gluma 2 Bond (2,7±1,2)=Ambar (2,9±1,2)<Single Bond Universal (3,5±1,5). Para o fator tempo o ΔE foi: 7 dias (1,7±0,7), 30 dias (3,5±1,2) e 12 meses (2,9±1,3). Pode-se concluir que os diferentes sistemas adesivos utilizados na cimentação de laminados cerâmicos de espessura fina influenciaram na cor final das restaurações. O momento da fotoativação, isolada ou simultânea ao cimento resinoso, não apresentou efeito significativo na estabilidade de cor dos laminados cerâmicos de espessura fina.

Bond strength at the cement/dentin interface according to protocols for final irrigation of post space

Aim: The aim was to evaluate the bond strength at the cement/dentin interface in the post space, after specimens were treated with different final irrigation protocols, followed by cementation with a dual resin cement. Methods: Forty-eight extracted uniradicular human premolars were divided into four groups according to the irrigation (n = 12): control with distilled water; 2.5% sodium hypochlorite (NaOCl) + ethylenediaminetetraacetic acid (EDTA); 2.5% NaOCl + passive ultrasonic irrigation (PUI); and 2% chlorhexidine (CHX). The pull-out test was performed. The results were evaluated using ANOVA with Tukey's paired comparisons, with a significance of 5%. Results: When all groups were compared, significant difference occurred (p = 0.006), and in the paired comparison, NaOCl + PUI and CHX differed (p = 0.005). The CHX showed significantly higher adhesive defects between cement and dentin than other groups. Conclusions: The final irrigation protocol for cleaning after preparation for post space directly influences the bond strength at the cement/dentin interface

Physicomechanical properties of different nanohybrid composites after aging: color stability, flexural strength, and microhardness

Aim: To evaluate the physicomechanical properties of different hybrid composites (Charisma Diamond - CD, Aura - AU, NT Premium - NT, Opallis - OP, Filtek Z250 ­ Z250) after 6 months of aging in distilled water. Methods: Discs were fabricated and color measurements were performed after 24 hours and at 7, 30, and 180 days. Flexural strength was determined using the three-point bending test. For the microhardness test, the specimens were flattened to obtain polished and flat surfaces and indentations. The results for ∆E and microhardness were analyzed by two-way repeated-measures ANOVA and Tukey's HSD test. The flexural strength results were analyzed by two-way ANOVA and Tukey's test (α=0.05). Results: The ∆E values for composite resins varied in the following order: CD (3.54)a < Z250 (4.70)ab < AU (4.95)ab < OP (5.20)ab < NT (6.23)b. ∆E values were lower for 24 h (3.84)a < 7 days (4.43)ab < 30 days (4.93)b. The highest values were observed after 180 days (ΔE = 6.54)c. The flexural strength of composite resins varied in the following order: CD (89.17 MPa)a < Z250 (73.06 MPa)b < OP (60.30 MPa)c < NT (51.28 MPa)c < AU (23.77 MPa)d. Flexural strength values were significantly higher for 24 h (68.62 MPa)a < 180 days (51.40 MPa)b. The microhardness of composite resins varied in the following order: Z250 (112.05)a < CD (102.15)ab < OP (92.04)bc < NT (87.77)d < AU (87.68)d. Microhardness was significantly higher for 180 days (113.44)a < 24 h (78.21)b. Conclusion: The microhybrid (Z250) and one of the nanohybrid composites (CD) performed better. The color stability and flexural strength of all tested composites decreased with storage time

Surface topography and bacterial adhesion of CAD/CAM resin based materials after application of different surface finishing techniques

Aim: This study evaluated the surface topography and bacterial adhesion of a hybrid ceramic and a nano ceramic resin composite after different surface finishes. Methods: Hybrid ceramic (Vita Enamic, VITA - EN) and nano ceramic resin composite (Lava Ultimate, 3M/ESPE - LV) blocks of 12 x 14 x 18 mm were cut into 1 mm slices. Each slice was divided into four specimens (6 x 7 mm) that were randomly allocated into 4 groups (n=8) according to the surface finishing: CTL - without surface finish (control); DB - wear with a diamond bur; VT - polishing system for hybrid ceramic (VITA); and DD - polishing system for ceramics (Dedeco). The specimens were analyzed regarding surface roughness parameters (Ra, Rz, Rq), sterilized and subjected to bacterial adhesion. Representative specimens from each group were observed by SEM and Confocal Laser Scanning Microscopy. Data were submitted to two-way ANOVA and Tukey's test (α=0.05). Results: EN had lower surface roughness and bacterial adhesion than LV (p<0.05), regardless of the surface finish. The highest values for all roughness parameters was observed in LVDB group, differing from the other groups, which were not significantly different. Smaller bacterial adhesion values (CFU/mL) were observed for ENDD and ENVT, which differed significantly from the other groups, except ENCTL. For LV groups there was no significant difference between the different surface finishes (p>0.05). The type of material and surface finish system significantly interfered with surface roughness parameters and bacterial adhesion. The hybrid ceramic performed better after polishing than the nano-ceramic resin. Conclusion: An adequate finishing/polishing technique should always be performed after any kind of adjustment to indirect restorations made with these materials tested

Long-term evaluation of crown and root discoloration induced by different endodontic sealers

Aim: To evaluate crown and root discoloration promoted by different endodontic sealers after root canal filling. Methods: Eighty bovine incisors were prepared and filled with: Endofill, Sealer 26, AH Plus, and MTA Fillapex. Color was recorded using a spectrophotometer before endodontic treatment (T0) and at 24 hours (T1), seven days (T2), 30 days (T3), and 90 days (T4) after treatment. Analyses were performed on the middle and cervical regions of the crown, and on the cervical third of the root, immediately below the cementoenamel junction. The color alterations (ΔE) were calculated using Commission International de I'Eclairage (CIE) L*a*b parameters, and data were analyzed by analysis of variance (ANOVA) and Tukey's test (p<0.05). Results: All sealers induced color alterations. Sealer 26 resulted in the smallest changes in color (E = 5.32). The other materials did not present statistical differences (AH Plus E = 6.98; MTA Fillapex E = 6.88; Endofill E = 6.41). Of the three regions analyzed, the largest discoloration was observed at the cervical third of the root (E=10.67). In terms of time, the largest ΔE values (E=7.72) were observed at T4. Color changes at T1 (E=5.88), T2 (E=6.10), and T3 (E=5.89) were statistically similar. Conclusions: All endodontic sealers promoted discoloration on the tooth crown and root

Effect of hydrogen peroxide and universal adhesive application on the bond strength of glass fiber posts

Aim: This study aims to evaluate the effect of different surface treatments on the bond strength of glass fiber posts. Methods: Ninety unirradicular premolars had their crowns removed and were endodontically treated. After 24h, post spaces were prepared and the roots (n=15) were divided into six groups according to the post surface treatment: NT ­ no treatment, UA ­ universal adhesive (Single Bond Universal), SUA ­ silane (Prosil), followed by universal adhesive, H ­ H2O2 (Whitness HP Maxx, 35%, gel, 1 min), HUA ­ H2O2, followed by universal adhesive, and HSUA ­ H2O2, followed by silane and universal adhesive. The posts were cemented with dual-cured resin cement (RelyX Ultimate). Bond strength was evaluated with pull-out test (0.5 mm/mim) after 24h-storage in distilled water at 37oC. Data were submitted to ANOVA and Tukey's test (α=5%). Results: HSUA group showed the highest bond strength value (236.5 N) followed by HUA (206.5 N), NT (194 N) and SUA (184 N) groups. UA group showed the lowest bond strength value (60 N). Conclusion: The use of H2O2, the silane application or the combination of these two treatments significantly increased bond strength values in groups in which the universal adhesive was used. A simplified procedure, such as cleaning with alcohol, can be recommended as surface treatment for the cementation of glass fiber posts (AU)

Physical properties of two bis-acryl interim materials: color stability, flexural strength and shear bond strength to flowable composite resin as add-on material

Aims: The objective of this study was to evaluate the mechanical properties of two bis-acryl interim resin materials, such as color stability, flexural strength and shear bond strength to flowable composite resin, simulating clinical situations when this material has to be used for repair as add-on. Two shades of two bis-acryl interim resin materials [Structur 2 SC (shades Bleach and A2); Protemp 4 (shades A1 and A2)] were evaluated. Discs (5 x 1 mm) were fabricated and baseline color was determined after 1 h. Ten specimens were immersed at 37oC in solutions of distilled water (control) and cola-based soft drink (Coca-Cola). Color measurements were performed with a spectrophotometer using CIELab parameters. Color readings were again measured after 2 hours, 4 hours, 24 hours and 7 days. Flexural strength was determined using the three-point bending test (10 x 1 x 2 mm) on a universal testing machine (0.5 mm/min) (n = 10). Discs of bis-acryl resin were embedded in acrylic resin, planned and distributed in 2 groups: G1 - Filtek Z350 Flow/Protemp4 and G2 - Grandio SO Flow/Structure 3 (n = 15). Cylinders (3.5 x 2 mm) were made with the flowable composite resins and polymerized for 20 s. The specimens were stored in distilled water at 37oC for 24 h and subjected to shear bond strength test. Data were analyzed using one-way ANOVA and Tukey's test (α = 0.05). ΔE values were higher for Structur Bleach (3.08)a compared with Protemp 4 (shade A1, 2.22)b (shade A2, 2.25)b. There were no significant differences between Structur Bleach and Structur A2 (2.62)ab. Coca-Cola presented higher ΔE values (3.08)a than (2.00)b. Regarding time, ΔE values increased from 1.84a after 2 h to 2.31b after 4 h. The higher values were observed after 24 h and 7 days (2.93c and 3.09d, respectively). No significant differences were observed for the flexural strength of Structur (22.05 MPa)a and Protemp 4 (19.01 MPa)a. The repairs executed with Structur/Grandio flow (9.21 MPa)a were similar to those performed with Protemp 4/Z350XT flow (10.71 MPa)a. It can be concluded that the two bis-acyl resins evaluated showed similar physical and mechanical properties (AU)

Marginal and Internal Adaptation of Zirconia Crowns: A Comparative Study of Assessment Methods

Abstract Marginal and internal adaptation is critical for the success of indirect restorations. New imaging systems make it possible to evaluate these parameters with precision and non-destructively. This study evaluated the marginal and internal adaptation of zirconia copings fabricated with two different systems using both silicone replica and microcomputed tomography (micro-CT) assessment methods. A metal master model, representing a preparation for an all-ceramic full crown, was digitally scanned and polycrystalline zirconia copings were fabricated with either Ceramill Zi (Amann-Girrbach) or inCoris Zi (Dentslpy-Sirona), n=10. For each coping, marginal and internal gaps were evaluated by silicone replica and micro-CT assessment methods. Four assessment points of each replica cross-section and micro-CT image were evaluated using imaging software: marginal gap (MG), axial wall (AW), axio-occlusal angle (AO) and mid-occlusal wall (MO). Data were statistically analyzed by factorial ANOVA and Tukey test (a=0.05). There was no statistically significant difference between the methods for MG and AW. For AO, there were significant differences between methods for Amann copings, while for Dentsply-Sirona copings similar values were observed. For MO, both methods presented statistically significant differences. A positive correlation was observed determined by the two assessment methods for MG values. In conclusion, the assessment method influenced the evaluation of marginal and internal adaptation of zirconia copings. Micro-CT showed lower marginal and internal gap values when compared to the silicone replica technique, although the difference was not always statistically significant. Marginal gap and axial wall assessment points showed the lower gap values, regardless of ceramic system and assessment method used.

Resumo A adaptação marginal e interna é fundamental para o sucesso das restaurações indiretas e novos sistemas de imagem permitem avaliar esses parâmetros de maneira não-destrutiva e com precisão. Este estudo avaliou a adaptação marginal e interna de copings de zircônia fabricados com dois sistemas diferentes, utilizando as técnicas da réplica em silicone e micro-CT. Um modelo-mestre de metal, representando um preparo para uma coroa totalmente cerâmica foi digitalizado e copings de zirconia policristalina (Ceramill Zi, Amann Girrbach e inCoris Zi, Dentslpy Sirona, n=10) foram fabricados. Para cada coping, a adaptação marginal e interna foi avaliada pelas técnicas da réplica em silicone e micro-CT. Foram avaliados quatro pontos de cada seção transversal e imagem de micro-CT: adaptação marginal (MG), parede axial (AW), ângulo axial-oclusal (AO) e parede centro-oclusal (MO) utilizando um software de imagem. Os dados foram analisados estatisticamente por ANOVA e teste de Tukey (a=0,05). Não houve diferença estatisticamente significativa entre as duas técnicas para MG e AW. Para AO, houve diferenças significativas entre as técnicas para copings da Amann, enquanto que para copings da Dentsply Sirona foram observados valores semelhantes. Para o MO, ambas as técnicas apresentaram diferenças estatisticamente significativas. Observou-se uma correlação positiva entre os valores de adaptação determinados pelas duas técnicas. O método de avaliação influenciou a avaliação da adaptação marginal e interna de copings de zircônia. Pode-se concluir que a micro-CT mostrou menores valores de adaptação marginal e interna quando comparado com a técnica de réplica em silicone. Os pontos de avaliação da margem e da parede axial mostraram os menores valores de adaptação, independente do sistema cerâmico e da técnica de avaliação utilizados.

Effect of Sonic Vibrations on Bond Strength of Fiberglass Posts Bonded to Root Dentin

Abstract Sonic vibrations may improve the bond strength and durability of fiberglass posts by improving adhesive penetration into dentin as well as the cement flow. The objective of this study was to evaluate the effect of sonic vibrations on the bond strength between fiberglass posts and root dentin using the pull-out test. Bovine roots were endodontically treated and divided randomly into four groups (n=12): Group C - conventional cementation (control); Group SA - sonic vibration (Smart Sonic Device, FGM) of the adhesive system and conventional post accommodation; SP group - conventional adhesive application and sonic vibration of the post during accommodation; and SASP - sonic vibration of the system adhesive and the post during accommodation. The posts were cleaned, treated with a silane and adhesive system (Ambar, FGM), and cemented with a dual-cured resin cement (Allcem Core, FGM). After 24 h, the specimens were subjected to mechanical tests and failure analyses. Representative specimens were analyzed by a scanning electron microscope to observe the cementation line. The results were analyzed using ANOVA and Tukey's test (a=5%). The bond strengths were as follows: SASP (90.9±27.1 N), C (121.4±60.6 N), SA (127.6±31.8 N) and SP (156.4±41.3 N). The use of sonic vibrations during the application of adhesive or post cementation separately did not affect the bond strength but had a negative effect when used for both procedures.

Resumo Vibrações sônicas podem melhorar a resistência e a durabilidade da união de pinos de fibra de vidro, melhorando a penetração do sistema adesivo à dentina, bem como o escoamento do cimento. O objetivo deste estudo foi avaliar o efeito da vibração sônica na resistência de união de pinos de fibra de vidro à dentina radicular, através de ensaio pull out. Raízes bovinas tratadas endodonticamente foram preparadas e divididas aleatoriamente em quatro grupos (n=12): Grupo C - cimentação convencional, (controle); Group SA - vibração sônica (Smart Sonic Device(r), FGM) do sistema adesivo e assentamento convencional do pino; grupo SP - aplicação convencional do sistema adesivo e vibração sônica no assentamento do pino; e SASP - vibração sônica do sistema adesivo e no assentamento do pino. Os retentores foram limpos, tratados com silano e sistema adesivo (Ambar, FGM) e cimentados com cimento resinoso dual (Allcem Core, FGM). Após 24 h as amostras foram submetidas ao teste mecânico e análise de falha. Amostras representativas foram avaliadas sob microscópio eletrônico de varredura, para avaliação da linha de cimentação. Os resultados foram analisados por meio de análise de variância e teste de Tukey (a=5%). Os resultados obtidos foram: SASP (90,9±27,1 N, C (121,4±60,6 N), SA (127,6±31,8 N) e SP (156,4±41,3 N). A vibração sônica para aplicação apenas do sistema adesivo ou pino não afetou a resistência de união, entretanto interferiu negativamente quando utilizada para ambos procedimentos.

Effect of Enamel and Dentin Surface Treatment on the Self-Adhesive Resin Cement Bond Strength

Abstract The aim of this study was to evaluate the effect of enamel and dentin surface treatment on the micro-shear bond strength of self-adhesive cement. Seventy-two extracted third molars had their crowns embedded in acrylic resin and worn to obtain a flat enamel or dentin surface. The enamel and dentin specimens were randomly assigned to 8 groups (n=12) that were based on surface treatment (11.5% polyacrylic acid solution or no treatment), substrate condition (wet or dry) and storage period (1 day or 90 days), and treated accordingly. Cylinders (1 × 1 mm) were fabricated using self-adhesive resin cement (RelyX U200) following the manufacturer's instructions. The specimens were stored in distilled water at 37 °C for either 1 day or 90 days and subjected to micro-shear bond strength test (EMIC DL 2000 at 0.5 mm/min). After this, the failure type of the specimens was determined. Data were subjected to statistical analysis (a=0.05). According to the results, the 11.5% polyacrylic acid application decreased the bond strength in both enamel and dentin samples. The moist groups showed higher bond strength than the dry ones, regardless of the substrate and surface treatment. Storage period did not influence bond strength. In conclusion, surface treatment with 11.5% polyacrylic acid and absence of moisture decreased the bond strength of the resin-cement (RelyU200), regardless of the storage period.

Resumo O objetivo do estudo foi avaliar o efeito de tratamentos de superfície em esmalte e dentina na resistência de união (RU) de um cimento auto-adesivo. As coroas de setenta e dois terceiros-molares foram incluídas em resina acrílica e desgastadas para obtenção de áreas planas em esmalte e dentina. Os espécimes de esmalte e dentina foram aleatoriamente distribuídos em 8 grupos (n=12) de acordo com: tratamento de superfície (sem tratamento ou aplicação de solução de ácido poliacrílico a 11,5%), condição do substrato (seco ou úmido) e período de armazenamento (1 dia ou 90 dias). Após, cilindros (1 x 1 mm) foram confeccionados na superfície dos espécimes utilizando cimento resinoso auto-adesivo (Rely X U200) segundo as instruções do fabricante. Os espécimes foram armazenados em água destilada a 37 oC por 1 dia ou 90 dias e submetidos ao ensaio mecânico de microcisalhamento (EMIC DL 2000 a 0,5 mm/min). O tipo de falha de cada espécime foi determinado após ensaio. Os dados foram submetidos à análise estatística (a=0,05). De acordo com os resultados, a aplicação de ácido poliacrílico a 11,5% diminuiu a RU em ambos substratos, esmalte e dentina. Os grupos mantidos úmidos mostraram maiores valores de RU do que os secos, independentemente do substrato ou tratamento de superfície. O período de armazenamento não influenciou nos valores de RU. Concluiu-se que o tratamento de superfície com ácido poliacrílico a 11,5% e a ausência de umidade no substrato diminuíram os valores de RU para o cimento resinoso auto-adesivo, independentemente do período de armazenamento.

Influence of the Resin Cement Thickness on the Push-Out Bond Strength of Glass Fiber Posts

Abstract The objective of the present study was to evaluate the influence of resin cement thickness on the bond strength of prefabricated and customized glass fiber posts after storage in distilled water. Thirty human uniradicular roots were treated endodontically. The roots were divided into 3 groups: THIN (thin cement layer) - post space preparation with #0.5 drill and cementation of #0.5 post; THICK (thick cement layer) - post space preparation with #1 drill and cementation of #0.5 post; and CUSTOM (customized cement layer) - post space preparation with #1 drill and cementation of a customized post (#0.5 glass fiber posts customized with resin composite). All posts were luted with self-adhesive resin cement. The push-out test was carried out after storage for 24 h and 90 days in distilled water at 37 °C. The data were analyzed with three-way ANOVA and Tukey's test (a=0.05). Bond strengths were significantly higher for CUSTOM (9.37 MPa), than for THIN (7.85 MPa) and THICK (7.07 MPa), which were statistically similar. Considering the thirds, the bond strength varied in the sequence: apical (7.13 MPa) < middle (8.22 MPa) = coronal (8.94 MPa). Bond strength for 24 h storage was significantly higher (8.80 MPa) than for 90-day storage (7.40 MPa). It may be concluded that the thickness of resin cement influenced the bond strength of glass fiber posts. The customized posts presented higher bond strength. Storage in water for 90 days affected negatively the values of bond strength, especially for thick cement layers in the apical third.

Resumo O objetivo deste estudo foi avaliar a influência da espessura da linha de cimento na resistência de união de pinos de fibra de vidro após armazenamento em água destilada. Trinta dentes humanos hígidos unirradiculares tiveram os canais tratados endodonticamente. As raízes foram distribuídas em três grupos: THIN (linha de cimento fina): conduto preparado com broca 0,5 e cimentação de pino 0,5; THICK (linha de cimento espessa): conduto preparado com broca 1 e cimentação de pino 0,5; e CUSTOM (linha de cimento personalizada): conduto preparado com broca 1 e cimentação de pino personalizada (pino 0,5 personalizado com resina composta). Os pinos foram cimentados com cimento auto-adesivo. Após armazenamento das raízes em água destilada a 37 °C por 24 h e 90 dias, o teste de cisalhamento por extrusão push-out foi realizado. Os resultados foram analisados estatisticamente por ANOVA a três fatores e teste de Tukey (a=0,05). A resistência de união foi significativamente maior para CUSTOM (9,37 MPa), do que para THIN (7,85 MPa) e THICK (7,07 MPa), que foram semelhantes entre si. Considerando-se os terços radiculares, a resistência de união variou na sequência: apical (7,13 MPa) < médio (8,22 MPa) = coronal (8,94 MPa). A resistência de união após 24 h de armazenamento em água foi significativamente maior (8,80 MPa) do que para 90 dias (7,40 MPa). Pode-se concluir que houve influência da espessura da linha de cimento na resistência de união de pinos de fibra de vidro, sendo que o uso de pinos personalizados apresentou maiores valores de resistência de união. O armazenamento em água por 90 dias afetou negativamente os valores de resistência de união, especialmente no terço apical, no grupo com linha de cimento mais espessa.

Influence of shade, curing mode, and aging on the color stability of resin cements

The color stability of resin cements is essential for aesthetic restorations. Aim: To evaluate the influence of shade and aging time on the color stability of two light-cured and two dual-cured resin cements. Methods: The CIE-Lab color parameters (n=6) were measured immediately after sample preparation and at 7, 30 and 90 days of aging in distilled water. The color difference (ΔE) was calculated and then analyzed by three-way ANOVA for repeated measures and Tukey's HSD test (α=0.05). Results: ΔE was higher for transparent resin colors, followed by dark and light colors. The mean values of ΔE were lower for both light-cured resin cements compared to the dual-cured cements. As the aging time increased, ΔE values increased. Conclusions: The light-cured resin cements showed greater color stability. The lighter shades of luting were more likely to display a greater color change...

Reestablishing aesthetic and function of patient with severe worn dentition: a conservative approach with provisional fixed tooth/implant supported prosthesis

Introduction:Patients with severe parafunctional habits can have a reduction of their occlusal vertical dimension (OVD) and may create complex cases of oral rehabilitation, in which the patient may develop occlusal, masticatory and psychological problems. Objective: To report a clinical case of restoration of masticatory function and aesthetics from the production of tooth/implant-supported prostheses with conservative preparations, reestablishing the OVD and occlusal stability.Case report: Patient MVN, 55 years old, wheelchair user, presenting bruxism with a history of gastric reflux due to hiatal hernia, attended the clinic at the University complaining of dental sensitivity, difficulty in chewing and aesthetic smile commitment. At clinical examination it was found widespread wear of teeth. Radiographic examination showed good periodontal health and dental implants in good condition of osseointegration. The OVD was established from the VDR and confirmed by the metric method. The initial casts were positioned on the articulator for diagnostic waxing. From the waxing it was possible to make provisional fixed tooth/implant-supported prostheses. In the lower arch, the prosthesis was screwed on the implants #35, #37, #46, and #47, with the remaining teeth working as an auxiliary support, while in the upper arch two interim prosthesis were made, one for the elements #16 and #17 (tooth-supported) and one for the elements #13, #12, #11, #21, #22, #23, #24 (tooth/implant-supported). Thus, the OVD and the aesthetics lost by bruxism abrasion were restored. Conclusion:This case demonstrates the importance of the provisional prostheses for aesthetic and functional rehabilitation of patients with severe worn dentition.

Microabrasion and composite resin for re-establishing smile esthetics: a case report

Introduction:Dental hypomineralization such as dental fluorosis has increased in recent times leading to unaesthetic appearance of teeth. There are different treatment possibilities to improve the aesthetic appearance of hypomineralized enamel described in dental literature. The enamel microabrasion has been a feasible alternative, since it is a fast, safe, conservative, and easy to perform, which promotes good esthetic results. Moreover, this technique is a conservative method that improves the appearance of the teeth by restoring bright and superficial smoothness, without causing significant structural loss. The association of different techniques, such as direct composite resin, can provide good esthetic outcomes, but the etiology, intensity, and depth of stain should be considered to minimize dental structure loss. Objective: To describe an easy technique for managing dental fluorosis using enamel microabrasion in association with direct composite resin. Case report: A mixture of hydrochloric acid and silicon carbide was applied according the manufacturer's instructions. Subsequently, a direct composite resin was applied over the areas where the opacities were more evident. This conservative approach may be considered an interesting alternative treatment to remove fluorosis staining and to improve aesthetic appearance. Conclusion: enamel microabrasion combined with direct composite resin is a conservative and safe alternative method to treat enamel opacities from dental fluorosis. Therefore, this management provides satisfactory aesthetic results for the patient's smile.

Silanated Surface Treatment: Effects on the Bond Strength to Lithium Disilicate Glass-Ceramic

Abstract: The aim of this study was to evaluate the effect of silanization protocols on the bond strength of two resin cements to a lithium disilicate glass-ceramic. Thirty-two ceramic discs were assigned to 2 groups (n=16): G1 - dual-cured resin cement and G2 - light-cured resin cement. Four subgroups were evaluated according to the used silanization protocol. The glass-ceramic was etched with 10% hydrofluoric acid for 20 s and silane was applied for 1 min, as follows: CTL - according to the manufacturer's instructions; HA - dried with hot air; NWA - washed and dried with water and air at room temperature; HWA - washed and dried with hot water and hot air. Thereafter, adhesive was applied and light-cured for 20 s. Silicon molds were used to prepare resin cement cylinders (1x1 mm) on the ceramic surface. The specimens were stored in deionized water at 37 °C for 48 h and subjected to a micro-shear test. The data were submitted to statistical analysis (?#61537;=0.05). Group G1 showed higher bond strengths than G2, except for the CTL and NWA subgroups. Differences as function of the silanization protocol were only observed in G1: HWA (25.13±6.83)≥HA (22.95±7.78)≥CTL(17.44±7.24) ≥NWA(14.63±8.76). For G2 there was no difference among the subgroups. In conclusion, the silanization protocol affected the resin cement/ceramic bond strengths, depending on the material. Washing/drying with hot water and/or hot air increased only the bond strength of the dual-cured resin cement.

Resumo: O objetivo do estudo foi avaliar o efeito da técnica de silanização na resistência de união de cimentos resinosos a uma vitrocerâmica. Trinta e dois discos de vitrocerâmica foram distribuídos em 2 grupos (n=16) (G1: cimento dual e G2: cimento fotoativado) e subdivididos em 4 grupos de acordo com a técnica de silanização. A vitrocerâmica foi condicionada com ácido fluorídrico a 10% por 20 s e o silano aplicado por 1 min de acordo com os subgrupos: CTL: de acordo com as instruções do fabricante, HA: secagem do silano com ar quente, NWA: lavagem e secagem com água e ar a temperatura ambiente, HWA: lavagem e secagem com água e ar quente. Após, o sistema adesivo foi aplicado e polimerizado por 20 s, e cilindros (1 x 1 mm) foram confeccionados com os cimentos sobre a superfície da cerâmica. Os espécimes foram armazenados em água destilada por 48 h e submetidos ao ensaio de microcisalhamento. Os dados foram submetidos à análise estatística (?#61537;=0,05). O grupo G1 apresentou maiores valores de resistência do que G2, exceto no subgrupo CTL e NWA. Houve diferença na técnica de silanização apenas para G1: HWA (25,13±6,83)≥ HA (22,95±7,78)≥ CTL (17,44±7,24)≥ NWA (14,63±8,76). Para G2 não houve diferença entre os subgrupos. Conclui-se que a técnica de silanização interferiu na resistência de união cimento/cerâmica dependendo do material utilizado. A lavagem e secagem com água e ar aquecidos promoveu maior valor de resistência apenas para o cimento dual.